CİVATA'LAR GENEL MEKANİK ÖZELLİKLERİ
GERİLME DİRENCİ-TENSİLE STRENGTH MPa ( N/mm2 )
| Civata Markaları | 3.6 | 4.6 | 4.8 | 5.6 | 5.8 | 6.8 | 8.8 | 8.8 | 10.9 | 12.9 |
|
|
<=16mm | >16mm | ||||||||
| Nominal değer | 300 | 400 | 400 | 500 | 500 | 600 | 800 | 800 | 1000 | 1200 |
| Minimum | 330 | 400 | 420 | 500 | 520 | 600 | 800 | 830 | 1040 | 1220 |
VİCKERS HARDNES HV
| Civata Markaları | 3.6 | 4.6 | 4.8 | 5.6 | 5.8 | 6.8 | 8.8 | 8.8 | 10.9 | 12.9 |
|
|
<=16mm | >16mm | ||||||||
| Minumum | 95 | 120 | 130 | 155 | 160 | 190 | 230 | 255 | 310 | 372 |
| Maximum | 220 | 220 | 220 | 220 | 220 | 250 | 300 | 336 | 382 | 434 |
BRİNELL HARDNESS HB
| Civata-Markaları | 3.6 | 4.6 | 4.8 | 5.6 | 5.8 | 6.8 | 8.8 | 8.8 | 10.9 | 12.9 |
|
|
<=16mm | >16mm | ||||||||
| Minumum | 90 | 114 | 124 | 147 | 152 | 181 | 219 | 242 | 295 | 353 |
| Maximum | 209 | 238 | 285 | 319 | 363 | 412 |
CİVATA'LAR SERTLİK DEĞERLERİ ROCKWELL HARDNESS HR
| Civata-Markaları | 3.6 | 4.6 | 4.8 | 5.6 | 5.8 | 6.8 | 8.8 | 8.8 | 10.9 | 12.9 |
|
|
<=16mm | >16mm | ||||||||
| Minumum HRB | 52 | 67 | 71 | 79 | 82 | 89 | ||||
| Minumum HRC | 20 | 23 | 31 | 38 | ||||||
| Maximum HRB | 95 | 95 | 95 | 95 | 95 | |||||
| Maximum HRC | 30 | 34 | 39 | 44 |
SURFACE HARDNESS HV -YÜZEY SERTLİĞİ
| Civata-Markaları | 3.6 | 4.6 | 4.8 | 5.6 | 5.8 | 6.8 | 8.8 | 8.8 | 10.9 | 12.9 |
|
|
<=16mm | >16mm | ||||||||
| Maximum | 320 | 356 | 402 | 454 |
YİELD STRESS MPa (N/mm2 ) -AKMA GERİLMESİ
| Civata-Markaları | 3.6 | 4.6 | 4.8 | 5.6 | 5.8 | 6.8 | 8.8 | 8.8 | 10.9 | 12.9 |
|
|
<=16mm | >16mm | ||||||||
| Nominal değer | 180 | 240 | 320 | 300 | 400 | 480 | ||||
| Minimum | 190 | 240 | 340 | 300 | 420 | 480 |
Çağlar Civata®